About our products: China united iron and steel limited is a company specialized in mild steel plate, Stainless steel plates, Stainless welded pipe, and seamless stainless pipes. Our supply capacity per year is about 8,900,000 tons stainless plate/coil according to ASTM A240, ASME SA240, JIS, AISI, EN, AND Other special requirements from our customer.

304l 1.4306

En 1.4306 / Aisi 304l

The chromium and nickel ranges are similar, nickel for each grades having an eight% minimal. This reduces the ferrite content of the metal and has found to be necessary for some chemical processes. Due to the marginally larger chromium and notably larger nickel content material, 1.4306 is extra corrosion resistant than 1.4307.

En 1.4306, Astm Type 304l

The European grades for the 316 and 316L types, 1.4401 and 1.4404, match on all elements with carbon ranges of 0.07% most for 1.4401 and 0.030% most for 1.4404. There are additionally excessive Mo variations (2.5% minimal Ni) of 316 and 316L in the EN system, 1.4436 and 1.4432 respectively. To further complicate mattters, there’s additionally grade 1.4435 which is each high in Mo (2.5% minimal) and in Ni (12.5% minimum). Stainless steel types1.4301 and 1.4307 are also called grades 304 and 304L respectively. It continues to be typically referred to by its old name 18/8 which is derived from the nominal composition of type 304 being 18% chromium and 8% nickel.

General Characteristics

  • In addition, the 18/8 Cr-Ni grades are susceptible to mechanical sawing, water slicing and all forms of thermal chopping (plasma and laser).
  • The 304 metal is characterized by full austenitic construction, low carbon content, excellent impression energy, formability and ductility, glorious weldability, non-magnetic properties and susceptibility to bending and machining.
  • Attention should also be paid to the excessive sharpening power of the fabric and susceptibility to crushing, primarily within the case of stainless-steel tapes, which after curing attain a power of N/mm2.
  • If higher power is required, greater carbon metal 1.4310 / AISI 301 is used.

It is suitable for contact with substances present in food manufacturing – tartaric acid, citric acid, oxalic acid, acetic acid, salicylic acid, vegetable preparations, alcohols, fermented products and other organic substances. To ensure that the weld steel properties (e.g. energy, corrosion resistance) are equivalent to those of the father or mother steel, matching or slightly overalloyed fillers ought to ideally be used. Core 304L/4306 has excellent A240 304L Stainless steel plate weldability and is appropriate for the full vary of standard welding methods (like MMA, MIG, MAG, TIG, SAW, LBW, or RSW), besides gasoline welding. Core 304L/4306 has about 50% higher thermal growth and decrease warmth conductivity compared to carbon steels. This implies that larger deformation and better shrinkage stresses could outcome from welding.

X5crni18-10, 1.4301, Aisi 304 – Specification And Application

The austenitic CrNi standard grades are the most extensively used group of stainless steels. Their nicely-balanced material properties make them suitable for the fabrication of many merchandise. This can result if the steel is held in a temperature range 450 to 850°C for periods of a number of minutes, relying on the temperature and subsequently uncovered to aggressive corrosive environments.

Despite its improved corrosion resistance, 1.4306 finds itself in a diminishing market so far as profiles is anxious. A attainable purpose for this might be that most profiles are subjected to additional processing by machining and thus far no NIRO-CUT® model exists. Most prospects thus specify both 1.4307 or 1.4404, when improved corrosion resistance is required. 1.4306 / AISI 304 L is an austenitic chromium-nickel stainless steel with a low carbon content material. As stainless steel, it withstands the working environment and make contact with with steam, water, ammonia, exterior situations, hydrogen sulphide, liquid fuels, sulphur, nitric acid, paints, phenols, some ammonium compounds and sulphates.

There are two European steels of the ‘304L’ type, 1.4306 and 1.4307. The 1.4301 and 1.4307 (304L) have carbon ranges of zero.07% most and zero.030% most, respectively.